Clear
A specialized photopolymer resin with high transparency for 3D printing with LCD devices. After fine polishing and applying a gloss oil, it achieves extremely high transparency, making it particularly suitable for scenarios requiring high transparency.
Features
- High transparency
- Excellent surface quality, smooth without layer lines
- Can withstand 70°C high-temperature treatment without cracking
- Appearance: Colorless transparent liquid
- Viscosity: 147 cps at 30°C
Material Description
Clear resin is perfect for Rapid Prototyping, creating transparent samples, crafting Display and Decorative pieces, and catering to the needs of 3D Printing enthusiasts.
Material Name ：Clear
Energy Density：3.6 mw/cm2
Layer Thickness：0.05 mm
Support Curing Time：8 seconds
Single Layer：30.66s/layer
Model Curing Time：6 seconds
50mm Part Printing Efficiency：8 hrs 30 mins 59 secs
Post-processing： Alcohol (95%) + Ultrasonic Cleaning for 4 minutes
Stickiness After Printing：No
Post-curing：UV Curing (405nm) for 10 minutes
Material TDS：Available
Stickiness After Curing：No
Mechanical Properties
We utilized the Martrix190 3D printer for the printing process, employing clear resin as the material. A total of 20 samples were printed, and the mechanical properties reported herein represent the average values across the sample set.
Tensile Strength: 39.0 MPa
Impact Strength: 20.8 J/m
Tensile Modulus: 1702 MPa
Shore Hardness: 78 D
Elongation at Break: 7.3%
Heat Deflection Temperature at 0.455 MPa: 45.8°C
Bending Strength: 53.5 MPa
Heat Deflection Temperature at 0.455 MPa: 42.1°C
Bending Modulus: 1682 MPa
Other Available Resins